A high-quality, high-deposition rutile flux-cored wire with an enhanced degree of fill for Argon/CO₂ gas mixtures. It is ideal for welding 355-460Mpa steels and thick steel components.The Taurus FCW E71T-H4 SPEC is a high-quality, high-deposition rutile flux-cored wire with an enhanced degree of fill for Argon/CO₂ gas mixtures. It is ideal for welding 355-460Mpa steels and thick steel components. The diffusible hydrogen level is consistently below 4ml/100g in deposited weld metal and since the seam of the wire is laser welded, there is no moisture pick-up. The wire is not copper coated and therefore there can be no contamination of feed liners, torches or contact tips resulting from copper flakes. It is designed for welding medium-strength steels (420MPa,61psi yield strength) using either 100% CO₂ shielding or Argon/CO₂ shielding gas mixture (15 – 25% CO₂ and balance Argon).
- All positional welding capabilities with outstanding performance in vertical-up welding of fillet and butt welds.
- Coefficient of flux fill and current capacity designed to deliver all positional weldability.
- Savings in welding cost resulting from easy slag removal and lack of spatters. Ideal for applications in shipbuilding and steel construction.
- Designed for mixed gas and the use of 100% CO₂ is possible.
TYPICAL APPLICATIONS
Hard-facing of hot cut-offs, shear blades, dies for pressure casting, scraper blades, conveyors, rollers, crusher rolls and worn parts in agricultural equipment.
WELDING POSITIONS
- Down hand
- Horizontal flat
- Horizontal vertical
- Vertical up
- Vertical down
- Overhead
CLASSIFICATIONS
- AWS A5.20: E71T-1 H4 / E71T-1M H4
- EN 758: T 46 2 P C 1 H5 / T 46 2 P M 1 H5
| COMPOSITION | % |
| Carbon | 0.05 |
| Manganese | 1.2 |
| Silicon | 0.55 |
| Sulphur | – |
| Phosphorous | – |
| MECHANICAL | AS WELDED |
| Yield strength (N/mm²) | ≥460 |
| Tensile strength (N/mm²) | 550-650 |
| Elongation A5 (%) | ≥22 |
| Impact Energy ISO – V (J) – 20°C | ≥ 80 |
AVAILABLE IN- 1.2mm – 15kg spool pack
- 1.6mm – 15kg spool pack