TAURUS MIG HRC360 is gas-shielded, high-alloyed, fluxcored wire designed for hard-facing deposit with high hardness. Especially developed for hard-facing of parts subjected to high metal to metal wear and moderate impact. Weld metal can retain its hardness at high temperatures up to 600°C. Weld metal can be grinded and machined by diamond tools. Weld metal is resistant to cracking and must not be welded more than 3 pass. If the base metal has a high carbon content and a low weldability, a tough buffer layer with FCW 30 is recommended before hard-facing. Heat treatment after hard-facing will decrease its welded hardness.
SOME FEATURES AND BENEFITS • Hard-facing deposit with high hardness of HRc 59.• Weld metal is resistant to cracking.
TYPICAL APPLICATIONS
Hard-facing of hot cut-offs, shear blades, dies for pressure casting, scraper blades, conveyors, rollers, crusher rolls and worn parts in agricultural equipment.
WELDING POSITIONS
- Down hand
- Horizontal flat
- Horizontal vertical
- Vertical up
- Vertical down
- Overhead
CLASSIFICATIONS
- EN 14700 T Fe8
- TS EN 14700 T Fe8
- DIN 8555 MF 6 GF 60 GP
| COMPOSITION | % |
| Carbon | 0.60 |
| Manganese | 0.20 |
| Silicon | 0.50 |
| Chromium | 5.6 |
| Molybdenum | 0.25 |
| Vanadium | 0.20 |
| Iron | Balance |
| MECHANICAL PROPERTIES | AS WELDED |
| Protection gas | CO2 |
| Wear Index | 70.2 |
| Hardness | 59 HRC |
AVAILABLE INTAURUS HRC58 HARD-FACING MIG WIRE
A shielded flux-cored wire for the hard-facing of parts subjected to extreme wear such as excavator parts, scraper blades, dipper teeth, worm conveyors, beaters, crusher jaws, crusher cones, subjected to heavy wear. The weld metal is tough, free of cracks and therefore resistant to shock and impact. Machining is only possible by grinding.
SOME FEATURES AND BENEFITS- Hard-facing deposit with high hardness of HRc 58.
- Weld metal is resistant to cracking, shock and impact.
WELDING POSITIONS
CLASSIFICATIONS| COMPOSITION | % |
| Carbon | 0.35 – 0.45 |
| Manganese | 1.50 – 2.50 |
| Silicon | 0.30 – 0.70 |
| Phosphorous | ≤ 0.030 |
| Sulphur | ≤ 0.030 |
| Chromium | 5.0 – 6.0 |
| Molybdenum | 1.4 – 1.6 |
| Vanadium | 0.4 – 0.5 |
| MECHANICAL PROPERTIES | AS WELDED |
| Hardness | 57 – 62 HRC |